Code：YT862
- Use：
● Fulfill the requirement of ROHS, REACH, BPA FREE
● Suitable for cold chain labeling applications.
- Mob：13602392761
-
Detail
Contact
Application
● Fulfill the requirement of ROHS, REACH, BPA FREE
● Minimum labeling temp: -25℃
● Service temp: -50℃~50℃ (24h after labeling)
● Suitable for cold chain labeling applications.
● At low temperature, the initial adhesion and final viscosity are good, and it has excellent performance on many packaging materials. Recommended for use at low temperatures
● Not suitable for applications in direct sunlight.
Print & Process
● Suitable for conventional printing.
● Alcohol or volatile organic solvent inks are not applicable.
● Not recommended to process die cutting in environment above 20℃.
Shelf life
| Facestock | |||
| Top coated thermal paper, with good performance at resistance of water, oil, plasticizer and scratch. | |||
| Indicator | Parameter | Unit | Method |
| Substance | 70±5% | g/㎡ | ISO 536 |
| Caliper | 72±5% | μm | ISO 534 |
| Optical | ≥1.10 | GB/T 28210 | |
| Adhesive | |||
| Freezing hot melt adhesive | |||
| This adhesive complies with FDA section 21 (175.105) and can be used for not-contact labeling of food, pharmaceutical and cosmetic products. | |||
| Liner | |||
| Super calendered white glassine | |||
| Indicator | Parameter | Unit | Method |
| Substance | 58±5% | g/㎡ | ISO 536 |
| Caliper | 51±5% | μm | ISO 534 |
| Tear Resistance | ≥300 | mN | GB/T 455 |
| Performance data | |||
| Indicator | Parameter | Unit | Method |
| Initial Tack | ≥11 or PT | N | FTM9，ss |
| 90 ° Peel Adhesion（20min） | ≥6 or PT | N/25mm | FTM2, ss |
| Shear Strength | ≥8 | hours | FTM8，ss |
| Low-temperature Loop Tack | ≥17 or PT | N | ±5℃，ss |